Please send us your inquiry about the customization of other furnace types or related questions about vacuum furnace. We will reply you immediately. Thank you.
Loading capacity: 4000kg
Max Temperature: 1350℃
Temperature Uniformity: ±5℃
Provide Customized Service
More Type
Loading capacity: 3000kg
Max Temperature: 2500℃
Temperature Uniformity: ±5℃
Provide Customized Service
More Type
Loading capacity: 5000kg
Max Temperature: 1350℃
Temperature Uniformity: ±5℃
Provide Customized Service
More Type
Loading capacity: 10,000kg
Max Temperature: 2500℃
Temperature Uniformity: ±5℃
Provide Customized Service
More Type
Downloads
All documents in the overview
News & Press
All news at a glance
Request
Send us a message
Email: contact@vacfurnace.com
Heat treatment : Frank +86 -188 5001 9186
Powder metallurgy: Jessica +86 -159 0193 1519
Address: NO.1299, XinJinQiao Road, Pudong New Area, Shanghai, China.
Copyright © 2010-2021 Shanghai Gehang Vacuum Technology Co.,Ltd. All Rights Reserved.
Preparation Of Tungsten Copper Alloy Contacts
Step 1: According to the mass ratio of CuO powder and W powder 1:1, mix the CuO powder and W powder evenly.
Step 2: Reduce the mixed powder at 450℃ under the atmosphere of hydrogen for 1h, then compacting, pressing and forming, and breaking it into powder. Then at the temperature of 700℃, under the atmosphere of hydrogen, reduction treatment for 1h, increase pressure to press molding, broken into powder;
Step 3: Put the mixed powder treated in step 2 into the compacted blank, place copper flakes above and below the compacted blank, and sintering for 3h at the temperature of 1100℃;
Step 4: Place the sintered material in a graphite container, and place the tungsten filament weaved body on the material and hold it in a vacuum at 1200℃ for 4 hours, that is the copper-tungsten contact material .